Available in 150~2000 mm length and 10~100 mm diameter, the offered Molybdenum Electrode is developed by adopting latest isotopic pressing technique which is followed by sintering in medium frequency furnace. The sintered electrode is later forged. We offer this item in different surface finishing options that include machine finished or centre less ground to maintain its straightness level. The offered electrode helps to maintain uniform temperature of the glass tank and helps to raise output as well as quality of glass. We are a reliable manufacturer of superior quality Molybdenum Electrode.
Features
Ability to endure high temperature
Long working life
Can resist oxidation caused by high temperature
Rust proof design
Application
The offered electrode is widely used in optical glass, glass fiber, daily glass, glass klin fore hearth, glass fiber furnace and insulation material production units. It is also required in rare earth industry.
More Key Points:
Shape : Angle
Hardness : 80-95 HRB
It is an Alloy
Color : Yellow
Warranty : As per contract
Surface Treatment : Polished
Technical Specification :
RWMA Group A
CuCr and CuCrZr
| Content (%wt.) | Density (g/cm3) | Conductivity (%IACS) | Hardness (HRB) | RWMA |
Cr: 0.6-1% | 8.9 | 70 | 85 | Class 2 |
Cr: 0.5-1.5%, Zr: 0.05-0.25%, Cu: balance | 8.9 | 80 | 80 | Class 2 |
Nickel Silicon Copper
| Composition | Density (g/cm3) | Conductivity (%IACS) | Hardness (HRB) | RWMA |
Si: 0.60-1.1% Ni: 2.4-3.4% Cu: balance | 8.83 | 40 | 90 | Class 3 |
CuCo2Be
| Content (%wt.) | Density (g/cm3) | Conductivity (%IACS) | Hardness (HRB) | RWMA |
Be: 0.40-0.70% Co: 2.40-2.70% Cu: balance | 8.83 | 45 | 95 | Class 3 |
RWMA Group B
Refractory Metal
Tungsten copper :
| Composition | Density (g/cm3) | Hardness (HRB) | Conductivity (%IACS) | RWMA |
W50Cu50 | 11.9 | 65 | 54 |
|
W55Cu45 | 12.5 | 70 | 49 | Class 10 |
W70Cu30 | 14.1 | 82 | 42 |
|
W75Cu25 | 14.5 | 90 | 38 | Class 11 |
W80Cu20 | 15.2 | 98 | 34 | Class 12 |
W85Cu15 | 15.9 | 240HB | 30 |
|
W90Cu10 | 16.75 | 260HB | 27 |
|
Tungsten
| Composite (%wt.) | Density (g/cm3) | Hardness (HRC) | Electrical Conductivity (%IACS) | Class | RWMA | Comparison |
W 99.95 | 19.3 | 36 | 30 | 13 | 13.743 | High temperature resistance |
W-Ce (CeO2:2%) | 19.2 |
|
|
|
| Low electric discharge power, fine arc-starting performance, excellent arc erosion resistance, longer service life |
W-La (La2O3: 1-2%) | 19.2 |
|
|
|
| Low electric discharge power, easy for machining |
Molybdenum
| Comparison (wt.%) | Density (g/cm³) | Hardness (HRB) | Electrical Conductivity (%IACS) | RWMA | Comparison |
Mo 99.95 | 10.2 | 90 HRB | 30 | 14.423 | Superior electrical and thermal conductivity |
TZM (Ti: 0.5%, Zr: 0.08%, C: 0.02%) | 10.17 |
|
|
| High thermal and creep resistance |
Mola (La2O3: 0.1 -1.8%) | 10.19 |
|
|
|
|