Developed from premium grade BeCu and copper, the offered Molybdenum Faced Electrode is notable for its silver white color. It possesses 2610oC melting point and high electrical conductivity level. Apart from that, this electrode is acknowledged for its low vapor pressure rate and good thermal conductivity level. The offered item has extensive utilization in different industries that include electronics, smelting, chemical processing, machinery and aerospace. As a growth oriented manufacturer, we are offering premium quality Molybdenum Faced Electrode which is accessible in different specifications.
Features
It has 2610oC melting point
High conductivity
It can prevent corrosion caused by glass and molten metal
Technical Specification :
RWMA Group A
CuCr and CuCrZr
| Content (%wt.) | Density (g/cm3) | Conductivity (%IACS) | Hardness (HRB) | RWMA |
Cr: 0.6-1% | 8.9 | 70 | 85 | Class 2 |
Cr: 0.5-1.5%, Zr: 0.05-0.25%, Cu: balance | 8.9 | 80 | 80 | Class 2 |
Nickel Silicon Copper
| Composition | Density (g/cm3) | Conductivity (%IACS) | Hardness (HRB) | RWMA |
Si: 0.60-1.1% Ni: 2.4-3.4% Cu: balance | 8.83 | 40 | 90 | Class 3 |
CuCo2Be
| Content (%wt.) | Density (g/cm3) | Conductivity (%IACS) | Hardness (HRB) | RWMA |
Be: 0.40-0.70% Co: 2.40-2.70% Cu: balance | 8.83 | 45 | 95 | Class 3 |
RWMA Group B
Refractory Metal
Tungsten copper :
| Composition | Density (g/cm3) | Hardness (HRB) | Conductivity (%IACS) | RWMA |
W50Cu50 | 11.9 | 65 | 54 |
|
W55Cu45 | 12.5 | 70 | 49 | Class 10 |
W70Cu30 | 14.1 | 82 | 42 |
|
W75Cu25 | 14.5 | 90 | 38 | Class 11 |
W80Cu20 | 15.2 | 98 | 34 | Class 12 |
W85Cu15 | 15.9 | 240HB | 30 |
|
W90Cu10 | 16.75 | 260HB | 27 |
|
Tungsten
| Composite (%wt.) | Density (g/cm3) | Hardness (HRC) | Electrical Conductivity (%IACS) | Class | RWMA | Comparison |
W 99.95 | 19.3 | 36 | 30 | 13 | 13.743 | High temperature resistance |
W-Ce (CeO2:2%) | 19.2 |
|
|
|
| Low electric discharge power, fine arc-starting performance, excellent arc erosion resistance, longer service life |
W-La (La2O3: 1-2%) | 19.2 |
|
|
|
| Low electric discharge power, easy for machining |
Molybdenum
| Comparison (wt.%) | Density (g/cm³) | Hardness (HRB) | Electrical Conductivity (%IACS) | RWMA | Comparison |
Mo 99.95 | 10.2 | 90 HRB | 30 | 14.423 | Superior electrical and thermal conductivity |
TZM (Ti: 0.5%, Zr: 0.08%, C: 0.02%) | 10.17 |
|
|
| High thermal and creep resistance |
Mola (La2O3: 0.1 -1.8%) | 10.19 |
|
|
|
|